2023-05-17 15:33:11 来源：钢铁之家阅读量：0

牌号	P295GH
欧标钢号	1.0481
对应标准	EN 10222-2-2017 压力用途用钢制锻件第2部分具有高温特性的铁素体和马氏体钢 Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
归类	碳钢

P295GH 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Ti	V	Nb	更多
最小值	0.08	-	0.9	-	-	-	-	-	-	-	-	-	Cr+Cu+Mo+Ni≤0.70
最大值	0.2	0.4	1.5	0.03	0.025	0.3	0.3	0.3	0.08	0.03	0.02	0.01	Cr+Cu+Mo+Ni≤0.70

碳当量计算

P295GH 机械性能

厚度 t mm	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	冲击吸收能量 KV2 J
t≤60	奥氏体化或固溶退火,890~950℃,空冷	460~580	≥285	I：≥24，tr/t：≥22	I：≥40，tr/t：≥27
60＜t≤100	奥氏体化或固溶退火,890~950℃,空冷	460~580	≥260	I：≥23，tr/t：≥21	I：≥40，tr/t：≥27

① I = longitudinal to main forging directions；tr = transverse to main forging directions；t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.

1 近似对照表承压扁钢制

国际标准组织	欧标
ISO	EN	数字牌号
P295GH	P295GH	1.0481

2 近似对照表碳素结构钢和工程用钢

日本	美国	国际标准组织	德国	法国	欧标		俄罗斯	瑞典	英国
JIS	ASTM	ISO	W-Nr.	NF EN/NF	EN	数字牌号	GOST	SS	BS EN/BS
SG365 SPV315 SPV32	A516Gr.65 X46	P11	1.0436	A48AP A48CP A48FP	P295GH	1.0481	14G2 18K	2102 2103	224-460B 224Gr.460 224Gr.490 430LT

注：本资料来源于互联网的公开资源整理，我们不保证这些资料的准确性、完整性和适用性。这些资料仅供您参考，不应用于任何商业用途或决策依据。本资料所记载的技术信息是说明产品的代表性特点和性能的参考值，对于因误用或不当使用本资料所记载的信息等而造成的损害恕难承担责任，敬请周知。